Storage Studies on Li/Graphite Cells and the Impact of So-Called SEI-Forming Electrolyte Additives
Notice bibliographique
Résumé
The growth of the solid electrolyte interphase on graphite electrodes during storage at different temperatures was studied using the High Precision Automated Storage System at Dalhousie University. The Li/graphite cells were precycled at 30°C before storage. The open circuit potential was automatically measured every six hours during storage and the capacity before and after storage was measured with high accuracy. The mechanism responsible for the capacity loss during storage is the growth and reformation of solid electrolyte interphase (SEI) on the graphite surface. The experimental results show that the addition of the electrolyte additives vinylene carbonate (VC) and fluoroethylene carbonate (FEC) increase the capacity loss during storage compared to the control electrolyte at 30, 40, 50 and 60°C. A beneficial effect of VC was not even observed at 60°C and cells with the FEC electrolyte additive showed substantially higher capacity loss at 60°C than control cells. Storage experiments on negative electrodes can lead to a better understanding of the solid electrolyte interphase and also can be used to screen for better SEI-forming electrolyte additives.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».