Structural and magnetic properties of NiMnSb/InGaAs/InP(001)
Notice bibliographique
Résumé
The structural and magnetic properties of NiMnSb films, 5–120 nm thick, grown on InGaAs/InP(001) substrates by molecular-beam epitaxy, were studied by x-ray diffraction, transmission electron microscopy (TEM), and ferromagnetic resonance (FMR) techniques. X-ray diffraction and TEM studies show that the NiMnSb films had the expected half-Heusler structure, and films up to 120 nm were pseudomorphically strained at the interface, greater than the critical thickness for this system, about 70 nm (0.6% mismatch to InP). No interfacial misfit dislocations were detected up to 85 nm, however, relaxation in the surface regions of films thicker than 40 nm was evident in x-ray reciprocal space maps. TEM investigations show that bulk, planar defects are present beginning in the thinnest film (10 nm). Their density remains constant but they gradually increase in size with increasing film thickness. By 40 nm these defects have overlapped to form a quasicontinuous network aligned closely with ⟨100⟩ in-plane directions. The associated strain fields and or compositional ordering from these defects introduced a reduction in crystal symmetry that influenced the magnetic properties. The in-plane and perpendicular FMR anisotropies are not well described by bulk and interface contributions. In thick films, the in-plane uniaxial and fourfold anisotropies increased with increasing film thickness. The lattice defects resulted in a large extrinsic magnetic damping caused by two-magnon scattering, an increase in the coersive field with increasing film thickness, and a lower magnetic moment (3.6 Bohr magnetons) compared to the expected value for the bulk crystals (4 Bohr magnetons).
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».