CdTeO x to CdTeO3 structural phase transition in as-grown polycrystalline films by reactive sputtering
Notice bibliographique
Résumé
Polycrystalline thin films of CdTeOx (x<3) and CdTeO3 were grown at 400 °C by rf-reactive sputtering. The CdTe oxide films were elaborated in an Ar–O2 atmosphere using different oxygen flow rates in the 5–11 SCCM (SCCM denotes cubic centimeter per minute at STP) range. The structural properties of the samples were studied by x-ray diffraction and micro-Raman spectroscopy. The diffraction patterns show that the films grown with oxygen flows between 5 and 10.5 SCCM present a crystalline structure similar to that of pure CdTe films, that is, a mixture of cubic zinc-blende-type and hexagonal wurtzite-type structures. However, the diffraction patterns of samples grown under an oxygen flow rate of 11 SCCM are strikingly different and in agreement with that of cubic CdTeO3, indicating that a structural phase transition was achieved. These results are in accordance with those obtained by micro-Raman spectroscopy, where the spectra of the CdTeOx samples grown with oxygen flows below 11 SCCM show an intense LO CdTe-like peak at 166 cm−1, which is no longer observable for the CdTeO3 sample. Instead, the Raman spectrum in this case is dominated by two broad bands in the 550–800 cm−1 range, which have been ascribed to the vibrational modes of TeO3 structural subunits. The optical properties, as determined by optical absorption and photoreflectance spectroscopies, are in correspondence with the structural and chemical changes induced by the incorporation of oxygen. The band gap varied between 1.55 and 3.3 eV, the last value corresponding to CdTeO3 films.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».