The Effect of Microstructure on Pit-to-Crack Transition and Crack Growth in an X-52 Pipeline Steel in Near-Neutral pH Environment
Notice bibliographique
Résumé
X-52 pipeline steel specimens that had been pitted using a passivation/immersion technique were cyclically loaded in a near-neutral pH solution sparged with 5% CO2/balance N2 gas mixture at a peak normal stress of 109% of the yield strength (YS), a stress ratio, R, of 0.8, and a frequency of 0.0001 Hz. Blunt cracks were seen to have initiated from the corrosion pits. There were many more cracks on the radial transverse (R-T) surface than on the axial transverse (A-T) surface. On the R-T surface, there were a lot of non-metallic inclusions particularly at mid-wall in this steel and these resulted in the nucleation of large pits that were particularly prone to pit-to-blunt-crack transition. At higher peak normal stress, 109% of YS, compared to previous studies at a little lower stresses, there was more rapid crack formation on the R-T surface. In the end, the cracks along the large elongated inclusions penetrated into the steel samples and led to failure. The crack path was transgranular in nature and the fracture surface displayed quasi-cleavage features. Analysis revealed that the pit depth to width ratio for individual pits was a little higher than that for linked pits, however, the ratio of crack depth to crack mouth width was observed to be much larger than the ratio for the linked pits. Strong preferential dissolution was believed to be responsible for the pit nucleation from these non-metallic inclusions, with the plastically deformed regions at the pits acting as the anodic phases.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».