Near-Neutral pH SCC of Two Line Pipe Steels Under Quasi-Static Stressing Conditions
Notice bibliographique
Résumé
Most published SCC results for the near-neutral pH condition were produced under cyclic loading. However, the presence of stress corrosion cracks in pipeline systems involving very small pressure fluctuations suggests the cracking should initiate and grow without large dynamic loads. This study was designed to investigate this issue. A Grade 448 (X-65) line pipe steel and a prototype Grade 550 (X-80) steel were evaluated in near-neutral pH solutions. The maximum stress applied was at 95% of the respective yield strengths and the R values applied were between 0.98 and 1.0. Two solutions were used for each steel: NS4 and NS4/clay mixture. The solutions were purged with a gas mixture of 95%N2 and 5%CO2. Recognizing that the crack propagation rate can be very slow under such near-static conditions, relatively long-term tests were carried out. The durations of the three tests using the prototype Grade 550 (X-80) steel were 110 days, 54 days and 26 days, and the duration for the X-65 steel was 110 days. After 110 days, the majority of the cracks in the Grade 550 (X-80) steel were in the range of 5 to 30 micrometers (μm) deep, giving an average crack propagation rate of 2*10−9 mm/s. Tests at short durations revealed that only a few cracks were detectable after 26 days and that several more cracks were produced after 54 days. So majority of the cracks in the 110-day were likely produced after 54 days of testing. The NS4/clay mixture was found to be less aggressive than the NS4 solution for both steels studied. The cracks in the prototype Grade 550 (X-80) steel were deeper and more numerous in comparison with the X-65 steel. Possible reasons for this observation are also explored in terms of the presence of martensite-austenite (MA) phase in the Grade 550 (X-80) steel.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,001 | 0,000 |
| Communication savante | 0,001 | 0,001 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,004 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».