Influence of Porosity on Performance of Freeze-granulated Fe2O3/Al2O3 Oxygen Carriers Used for Chemical Looping Combustion
Notice bibliographique
Résumé
Chemical looping combustion (CLC) is a promising solution for the next coal-fired power generation technology with inherent CO2 separation capability. One of the critical aspects for the development of the CLC process is to develop suitable oxygen carrier (OC) particles to transfer oxygen to the fuel in the absence of air. Relevant studies have focused on active material screening, thermodynamic analysis and operational tests. This investigation was conducted on the microstructural property of OCs, to be specific, the particle porosity effect on the performance of iron-based OCs. Fe2O3, supported on Al2O3 was used as the oxygen carrier. The effect of water content of the spray slurry used to produce the OC was varied to determine the influence of OC porosity on reactivity, oxygen transfer capacity and mechanical durability. A preliminary test was done to establish the minimum and maximum water percentage needed to make slurry. A process that included freeze granulation (FG), freeze drying, and calcination was used to prepare four samples of iron oxide/alumina with various water-to-solid phase ratios. A scanning electron microscope (SEM) was used to characterize the porosity of FG Fe2O3/Al2O3 particles. A direct relationship was observed. A Shimpo FGE-10X force gauge was used to measure the crushing strength of selected samples. A thermogravimetric analyzer (TGA) coupled with a mass spectrometer (MS) was used to study the change in reaction rates through multiple reduction-oxidation cycles of the samples. Crystallinity of the OCs in reduced and oxidized forms were confirmed by XRD analysis.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».