Experimental Study on SCC Susceptibility of X60 Steel Using Full Pipe Sections in Near-Neutral pH Environment
Notice bibliographique
Résumé
Stress corrosion cracking (SCC) tests were performed using the pipe section buried in a clay type of soil with the pH adjusted to near-neutral range. Pipe specimens with various sizes of fatigue pre-cracks ahead of artifical notch tips on the outer surface were subjected to cyclic loading tests. Maximum level of hoop stress was 105% SMYS, and R-value (Ratio of minimum load to maximum load) was 0.5. Growth of cracks was observed from the fatigue crack tips. Fractographic and metallographic examination has confirmed the quasi-cleavage nature of the transgranular SCC that is typically observed in near-neutral pH SCC. Crack depth measurement using DCPD method revealed the relatively high crack growth rate up to 10−5 mm/s. Metallographic examinations showed the existence of many micro-cracks associated with MnS inclusions in the highly strained field ahead of the initial crack tips. The relatively high crack growth rate may be caused by MnS inclusions. The loading rate, dJ/dt, was calculated for each crack condition in order to correlate qualitatively the crack growth rate with the loading rate. J-integral was calculated through non-linear FEM analyses for semi-elliptical cracks based on the stress-strain relationships obtained from the tensile tests using the same X60 steel specimen. Linear relationship was then obtained between the crack growth rate and the loading rate, and therefore the possibility to predict crack growth rates for various loading condition in the field was demonstrated.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».