Microscopic Cracking on Flat Alloy 600 Surfaces Following Accelerated Caustic Corrosion: Mapping of Strains and Microstructure During the Corrosion Process
Notice bibliographique
Résumé
Microscopic distributions of elastic and plastic strains have been studied at three intervals during an electrochemically accelerated corrosion test of a flat, polished surface of a mill-annealed and unstrained sample of Alloy 600 (UNS N06600) in 10% sodium hydroxide (NaOH) at 315°C. Laue microdiffraction was used with a micron-sized polychromatic (white) x-ray beam to map strain changes in the sample as a function of corrosion time. After two 12 h corrosion periods, tensile elastic strains were detected along a grain boundary. After a third 24 h corrosion period, this particular boundary was found to have cracked to a depth of several microns; other adjacent boundaries exhibited tensile elastic strain, but no cracking. No significant changes to plastic strain distributions in the same area could be detected as a function of corrosion exposure.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,001 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,001 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».