Experimental Evaluation of Fatigue Life of Coke Drum Materials With Weld Sections
Notice bibliographique
Résumé
Coke drums are vertical pressure vessels used in the delayed coking process in petroleum refineries. Significant temperature variation during the delayed coking process causes damage in coke drums in the form of bulging and cracking. It was also observed that most cracks were near or within the weld seams. In order to better understand fatigue damage mechanisms of the coke drum materials with their weld sections, an experimental investigation of fatigue lives of these materials are carried out. It is a common consideration that the yield strength of the weld should be within a close percentage to that of base material in order to keep strength uniformity throughout the drum shell sections. However, this effect of the yield strength matching on the shell durability has not yet clarified quantitatively. From this point of view, two different types of specimens have been designed and manufactured: base material only, base with base weld. In addition, three groups of base with weld materials with different ratios of weld to base yield strengths are prepared. Low cycle fatigue tests at elevated temperature of 250°C are carried out on the above specimens. Through study on the recorded stress-strain hysteresis loops and observation on the fracture surfaces, damage mechanisms of different types of specimens are analyzed. Their strain range–fatigue life curves are also compared. Furthermore, finite element analyses based on the actual specimens’ geometries and properties are conducted to help in understanding the experimental observations. This experimental evaluation of fatigue life of coke drum materials with welds may provide a good reference for better design of coke drums in the future.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,001 |
| Méta-épidémiologie (sens strict) | 0,001 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,001 | 0,001 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,001 | 0,000 |
| Intégrité de la recherche | 0,001 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,002 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».