Non-destructive inspection of welding defects in friction stir welds and prediction of their fatigue life
Notice bibliographique
Résumé
The welding defects in friction stir welds (FSW) such as kissing bond and wormhole were inspected by non-destructive techniques based on X-ray inspection and ultrasonic testing with phased-array probe. Although the X-ray inspection could detect wormhole defects, kissing bonds were recognized only by the ultrasonic testing. The sizes of kissing bonds were estimated based on the maximum echo height of the ultrasonic testing, while the estimated sizes were smaller than the actual ones observed on the fatigue fracture surfaces. Fatigue tests were performed using welds with defects, revealing that the fatigue strengths were significantly reduced due to the early fatigue crack initiation from defects. The prediction of fatigue life of weld was conducted based on the Paris law of fatigue crack propagation rate. The predicted lives of the welds with defects correlated with the actual ones. The ultrasonic testing led to the linear relationship between the estimated and actual sizes of kissing bond, thus it would be possible to predict the fatigue life of the weld with defects by non-destructive inspection.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,001 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».