Electrolytic Deposition of Oxide coatings for Solid Oxide Fuel Cell Interconnects
Notice bibliographique
Résumé
Composite yttria-silver coatings and praseodymia coatings were applied to 430 stainless steel by cathodic electrolytic deposition. Crack-free 0.5–1 μm thick coatings were obtained from chloride salts in aqueous or water-ethanol solutions. The electrical conductivity and oxidation behavior at 750°C of coated and uncoated samples were investigated. Coated samples oxidized for 24 h developed a scale thickness of approximately 1 μm and an area-specific resistance (ASR) of less than 0.1 ohm-cm2, compared to uncoated samples which had a scale thickness near 1.3 μm and an ASR near 0.2 ohm-cm2. The scale growth followed parabolic oxidation kinetics up to 168 h, spalling of the scale was evident. Another group of coated samples was initially heated in intermittent steps to 750 C over a period of hours. These samples showed better oxidation performance with good scale adhesion and had a scale thickness of less than 0.1 μm and an ASR of less than 0.1 ohm-cm2.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,001 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».