Role of Prior Cyclic Loading in the Initiation of Stress-Corrosion Cracks on Pipeline Steels Exposed to Near-Neutral pH Environment
Notice bibliographique
Résumé
X-52 and X-80 pipeline steels have been used to study the effect of cyclic loading prior to corrosion exposure upon the initiation of stress-corrosion cracks in a near-neutral pH environment. To simulate realistic loading conditions, a cyclic loading scheme was constructed based on pressure fluctuation data collected on operating pipeline systems. It has been observed that cyclic loading either prior to corrosion exposure under static stress or during corrosion exposure enhances pitting corrosion and micro-cracking on the steel surface. These pits are seen to be aligned along scratches on the steel surface and to have coalesced to form micro-cracks at some locations. Some micro-cracks appeared not to have developed from pits, but were instead observed in a direction approximately 45 degree to stress axis. They are believed to have developed at locations where localized deformation such as persistent slip bands has occurred due to cyclic loading. In contrast to cyclic loading, no pits or micro-cracks were seen on the specimen that was subjected to static loading only. The pits and micro-cracks were only observed when the specimens were immersed under a cathodic potential of −790 mV SCE. At the open circuit potential only uniform corrosion occurred on the specimens whether they were cyclically or statically stressed.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,003 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».