Degradation of Metal-Supported Cells with Ni-YSZ or Ni-Ni<sub>3</sub>Sn-YSZ Anodes Operated with Methane-Based Fuels
Notice bibliographique
Résumé
Ni-Ni3Sn-YSZ and Ni-YSZ anodes were incorporated into metal-supported SOFCs that consisted of a porous metal support (Sandvik Sanergy), samaria-doped ceria (SDC) barrier layer, anode as previously described, YSZ electrolyte, and La0.6Sr0.4Co0.2Fe0.8O3-δ-SDC cathode. Cells were tested at 750°C with air as the oxidant and fuel consisting of 65% CH4, 32% H2, and 3% H2O. The cells were held at a current density of 0.15 A·cm-2 for 500 hours. The cell without tin in the anode began to degrade after approximately 200 hours and catastrophically failed at approximately 425 hours. After testing, we observed that the anode had disintegrated, and as a result, the electrolyte and cathode were completely detached from the metal support. On the other hand, the cell with an anode containing tin did not catastrophically fail, and the cell remained intact after 500 hours of operation. Over 500 hours, the cell potential degraded from 0.841 V to 0.743 V, and scanning electron micrographs showed that the anode had delaminated from the electrolyte in some areas. Nonetheless, the cell with the Ni-Ni3Sn-YSZ anode degraded significantly less than the cell containing a Ni-YSZ anode, suggesting that the addition of Ni3Sn to an anode could be a useful strategy for improving durability of SOFC anodes using hydrocarbon fuels.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,001 | 0,001 |
| Communication savante | 0,000 | 0,001 |
| Science ouverte | 0,001 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,002 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».