Damage to an A-N720 ceramic matrix composite under simulated gas turbine static component conditions using laser heating
Notice bibliographique
Résumé
A ceramic matrix composite material constructed from a porous alumina matrix and Nextel™ 720 fibers was subjected to a novel type of experiment designed to reproduce the operating conditions of a gas turbine static component. Material specimens were exposed to cyclic laser heating on one side and active air cooling on the other side while being constrained in their bending deflection. For most specimens, accumulation of damage under the constant-amplitude heat load resulted in a temperature increase above the material limit of 1200℃ at the heated surface. Stress relaxation was observed due to inflicted sudden damage, like surface fiber buckling or ply delamination, and due to gradual permanent deformation of the material. The amount of damage was quantified by the variation of a stiffness parameter based on the measured reaction force and through-thickness temperature difference. While the level of damage was significant at the hot face, with the depth of cracking and delamination reaching up to half of the specimen thickness, the specimen back face remained intact. Stabilization of the damage was observed due to stress relaxation and decoupling of the damaged plies from the non-affected ones.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».