Structure and Mineralogy of Hydrophilic and Biwettable Sub-2 µm Clay Aggregates in Oil Sands Bitumen Froth

A primary concern of commercial mined oil sands operations is the extent to which one can minimize the content of water and solids contaminants in the solvent-diluted bitumen products resulting from the bitumen production processes. During bitumen production, particles of about 2 µm or less may be responsible for the stabilization of water-in-bitumen emulsions that form during aqueous extraction of bitumen and purification of bitumen froth subsequently during the froth treatment processes, thus leading to the presence of those contaminants in solvent-diluted bitumen products. In this study, we separate and analyze sub-2 µm clay solids isolated from typical bitumen froth fed to a froth treatment plant at a commercial mined oil sands operation. Analytical transmission electron microscopy (TEM) with spatially-resolved energy-dispersive X-ray spectroscopy (EDX) and electron energy-loss spectroscopy (EELS) demonstrate key differences in morphology and composition between sub-2 µm clay aggregates with two distinct wettability characteristics: hydrophilic vs. biwettable particle surfaces. In particular, clay platelets with <200 nm lateral dimensions and thicknesses of a few atomic layers, which are intermixed within coarser sub-2 µm clay aggregates, are found to confer clear differences in morphological characteristics and wettability behaviors to the sub-2 µm clay aggregates. The <200 nm clay platelets found within sub-2 µm biwettable clays tend to arrange themselves with random orientations, whereas <200 nm clay platelets within sub-2 µm hydrophilic clays typically form well-ordered face-to-face stacks. Moreover, in biwettable sub-2 µm clay aggregates, <200 nm clay platelets often cover the surfaces of ~1–2 µm sized mineral particles, whereas similarly sized mineral particles in hydrophilic sub-2 µm clay aggregates, in contrast, generally have exposed surfaces without clay platelet coverage. These biwettable vs. hydrophilic behaviors are attributed to a difference in the surface characteristics of the <200 nm clay platelets caused by toluene-unextractable organic carbon coatings. Nanometer-scale carbon mapping reveals an inhomogeneous toluene-unextractable organic carbon coating on the surfaces of <200 nm platelets in biwettable clays. In contrast, hydrophilic clays have a significantly lower amount of toluene-unextractable organic carbon, which tends to be concentrated at steps or near metal oxide nanoparticles on clay particle surfaces. Mixing surface-active organic species, such as asphaltene, resin, or carboxylic organic acids of various types with inorganic solids can lead to a dramatically enhanced emulsion stability. Consequently, understanding the origin and characteristics of sub-2 µm clay solids in bitumen froth is important to (i) clarify their potential role in the formation of stable water-in-oil emulsions during bitumen production and (ii) improve froth treatment process performance to further reduce contaminant solids in solvent-diluted bitumen products. We discuss the implications of our results from these two perspectives.

Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.