The Effect of Periodic Overloads on Biaxial Fatigue of Normalized SAE 1045 Steel
Notice bibliographique
Résumé
During the past decade it has been observed that periodically applied overloads of yield stress magnitude can significantly reduce or eliminate crack closure under uniaxial or Mode I loading. This paper reports the results of a series of biaxial in-phase tension-torsion experiments that were performed to evaluate the effects of overloads on the fatigue life of smooth tubes constructed of normalized SAE 1045 steel. Five strain ratios were investigated, including uniaxial (λ = εxy/εxx = 0), pure torsion (λ = ∞), and three intermediate ratios (λ = 3/4, 3/2, and 3). Periodically applied overloads of yield stress magnitude allowed cracks to grow under crack face interference-free conditions. Strain-life curves were developed by computationally removing the overload cycle damage from test results and calculating equivalent fatigue lives. A factor of two reduction in the fatigue limit was found at all ratios when these results were compared with constant-amplitude results. Cracking behavior was observed and it was noted that for strain ratios greater than one, cracks initiated along the rolling direction (longitudinally); otherwise, the cracks initiated on maximum shear planes. This observation was used to help explain the similarity in fatigue life results for all strain ratios for both constant-amplitude and overload data. Parameter-life curves were developed using the equivalent fatigue life data and several common multiaxial damage parameters, and the damage parameters were evaluated. It was found that the simple maximum shear strain criterion together with uniaxial overload data provided a good estimate of the fatigue behavior for all strain ratios.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».