Corrosion Behavior of Thermal Seamless Carbon Steel Boiler Pipes
Notice bibliographique
Résumé
The current study was absorbed on corrosion of ASTM A106 grade B -02 seamless carbon steel boiler pipes. Beyond corrosion experiments in corrosive medium with varying pH values, the weight lost in addition to corrosion rate (m.p.y) values were computed. The weight loss of boiler tube specimens exposed to corrosive liquid was shown to rise as the exposure period of the specimens increased. The results of the microstructure imaging showed that a de-carburized film of 240 µm thickness was shaped on the fireside of the pipe boiler, with ferrite and a few phases of pearlite. On the water lateral side, it was revealed that boiler pipe failure begins with small rust particles that expand to greater sizes and form scales that are displaced from the boiler pipe's surface. On the surfaces of the boiler pipe water side, several pits with crevice corrosion were observed. The corrosion amounts were discovered to decrease when the specimens' exposure time to corrosive environments and hydrogen ion concentration contents increased (pH). The findings of mechanical characteristic values such as hardness, yield strength, and tensile strength revealed that the waterside had higher values than the fireside, while the middle of the pipe had reasonable values. The findings also demonstrated that at low pH values, a tiny size of rust was created on the boiler tube specimen surface. However, at high pH values of corrosive medium, big sizes of corrosion rust were observed on the specimen surfaces.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,001 |
| Études des sciences et des technologies | 0,000 | 0,001 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,001 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».