Alloying of Cold-Sprayed Al-Ti, Al-Ni Composite Films
Notice bibliographique
Résumé
Abstract The Al-Ti, Al-Ni mixed powders were successfully coated by cold gas dynamic spray process (CDSP) and alloying behaviors of films after post-annealing were investigated. The particles were accelerated through a standard de Laval type of nozzle with 120psi (prior to enter). Instead of conventional He gas, the air was used as particle carrying gas. The as-purchased power size of Al, Ti, Ni, was 77, 44, and 3, respectively. The composition of Ti and Ni was varied from 10 and 30 wt%. The coated films were annealed at 600~630. in air or N2 atmosphere for 3 hrs. It was observed that Ni and Ti particles were finely dispersed and imbedded densely in Al matrix. After post annealing of Al-Ti and Al-Ni films, alloy phases such as the Al3Ti and Al3Ni phase were formed in the films. In case of Al-Ni films after annealing in air, the oxidation process seemed to retard the alloying of Al3Ni. However, after annealing in N2, the limitless alloying was proceeded until Ni particles were all consumed. In case of Al-Ti films, it was found that oxidation were virtually nonexistent even in air atmosphere. The formation of Al3Ti seemed to be limited by Al or Ti diffusion via preformed Al3Ti phase encapsulating Ti powder. In bond strength test, Al-Ti and Al- Ni composite films have higher adhesive bond strength up to 2~ 3 times more than pure Al coating due to massive crater formation of hard Ni or Ti particles. In conclusion, CDSP of Al-metal composite powder source can be a practical and economical way to prepare hard and adhesive Al-alloy thick films owing to stable and finely dispersed inter metallic compound formed in low Temperature annealing. Abstract only; no full-text paper available.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».