Microstructural characterization and mechanical properties of AlMg alloy fabricated by additive friction stir deposition
Notice bibliographique
Résumé
Abstract This work investigates microstructure characterization and mechanical properties of Aluminum alloy fabricated by additive friction stir deposition (AFSD). Microstructure characterize of the Aluminum alloy 5B70 base material (BM) and build were compared using optical microscope (OM) and electron back scattered diffraction (EBSD). Hardness distribution in the direction perpendicular to the cross-section of deposited area was measured and the pattern was evaluated. Tensile tests were performed on the BM and the deposition using digital image correlation (DIC), and the stress distribution states of the specimens were analyzed in real time. After the tensile tests, the fracture micromorphology was characterized using scanning electron microscope (SEM). The results show that a high degree of recrystallization of the grains in the deposition zone occurs and fine equiaxed grains are formed, which are oriented differently. In tensile tests on the deposition, it was found that the strength of the deposition was significantly lower compared to the BM, but its toughness was significantly higher. And there is a significant anisotropy in the mechanical properties of the deposition.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,001 |
| Intégrité de la recherche | 0,000 | 0,001 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».