Effect of Using Manufacturer-recommended Exposure Times to Photo-activate Bulk-fill and Conventional Resin-based Composites
Pourquoi ce travail est dans la base
Une base qui oublie comment elle a trouvé un travail ne peut pas être vérifiée. Voici les voies qui ont admis celui-ci.
Notice bibliographique
Résumé
OBJECTIVES: To analyze the effect of using the resin-based composite manufacturer's recommended exposure time on the degree of conversion (DC), Knoop hardness (KH), and elastic modulus (E) of conventional and bulk-fill resin-based composites (RBCs). METHODS: Three resin-based composites (RBCs) were tested: Tetric EvoCeram Bulk Fill (TET), Opus Bulk Fill APS (OPU), and RBC Vittra APS (VIT). They were photo-activated in 2 mm deep, 6 mm diameter molds for their recommended exposure times of 10 seconds, 20 seconds, or 40 seconds from four light-curing units (LCUs). Two delivered a single emission peak in the blue light region (Optilight Max and Radii-Cal) and two delivered multiple emission peaks in the violet and blue region (VALO Cordless and Bluephase G2). After 24 hours of dry storage at 37°C in the dark, the KH (Kgf/mm2), E (MPa) and DC (%) at the top and bottom surfaces of specimens (n=5) were measured and the results analyzed by 2-way analysis of variance (ANOVA) followed by a Tukey test (α=0.05). RESULTS: The irradiance (mW/cm2) and spectral irradiance (mW/cm2/nm) from the LCUs were reduced significantly (8-35%) after passing through 2.0 mm of RBC (p<0.001). The DC at the bottom of VIT and TET was less than at the top surface (p<0.001). OPU had the same DC at the top and bottom surface (p=0.341). The KH and E values at the top surface of VIT and TET were substantially higher than at the bottom (p<0.001). OPU exposed for 40 seconds achieved higher mechanical properties than TET that was photo-activated for 10 seconds (p<0.001). The opacity of different bulk-fill RBCs changed differently during the polymerization; OPU became more opaque, whereas TET became more transparent. When exposed for their recommended times, the 2 mm thick RBCs that used Ivocerin or the APS photoinitiator system were adequately photo-activated using either the single or multiple emission peak LCUs (p=0.341). CONCLUSION: After 24 hours' storage, all the 2 mm thick RBCs photo-cured in 6 mm diameter molds achieved a bottom-to-top hardness ratio of at least 80% when their recommended exposure times were used. TET, when photo-activated for 10 seconds, achieved lower mechanical properties than OPU that had been photo-activated for 40 seconds. The change in opacity of the RBCs was different during photo-activation.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découle