Fabrication of flat stainless steel substrates with improved oxidation behavior for metal-supported solid oxide cells using aqueous tape casting
Notice bibliographique
Résumé
Abstract An aqueous tape casting procedure was developed and optimized to fabricate thick, flat tapes for use as porous stainless-steel substrates for metal-supported solid oxide cells (MS-SOCs). Curling tape is one of the main challenges when using aqueous based slurry formation. This work demonstrated that the sedimentation problem can be solved by increasing solid loading rather than adding excessive binder to raise viscosity. The effect of various casting surfaces on tape curling was also investigated. Materials that allow easy tape release resulted in flatter tapes once the water was evaporated. In addition, substrate oxidation resistance at high temperature was evaluated with respect to starting powder size, sintering extent, and pore former types. High sintering extent that removes or encloses the porosity between steel particles while retaining porosity left by pore formers can effectively prevent breakaway oxidation due to local chromium depletion. Carbon residue in the steel substrates from the slurry organic content can be decreased when formulating the slurry to prevent Cr-rich phase formation in the steel, which severely compromises the substrate oxidation resistance and ductility. By dwelling the substrate in high purity hydrogen, the sensitization can be reversed, but more detailed investigation of the reaction dynamics is needed. By combining the strategies described, this work produced crack-free, flat, 400–500 μm thick stainless steel substrates with 28.7 vol% porosity and improved oxidation resistance compared to previous substrates fabricated by dry pressing of fine powders.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,001 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».