Synthesis and Transport Properties of ZnSnP2-yAsy Chalcopyrite Solid Solutions
Notice bibliographique
Résumé
This work focuses on the synthesis and properties of quaternary ZnSnP2-yAsy chalcopyrite solid solutions. Full miscibility of the solid solution is achieved using ball milling followed by hot press sintering. The measured electrical conductivity increases substantially with As substitution from 0.03 S cm−1 for ZnSnP2 to 10.3 S cm−1 for ZnSnAs2 at 715 K. Band gaps calculated from the activation energies show a steady decrease with increasing As concentration from 1.4 eV for ZnSnP2 to 0.7 eV for ZnSnAs2. The Seebeck coefficient decreases significantly with As substitution from nearly 1000 μV K−1 for ZnSnP2 to −100 μV K−1 for ZnSnAs2 at 650 K. Thermal conductivity is decreased for the solid solutions due to alloy phonon scattering, compared to the end members with y = 0 and y = 2, with the y = 0.5 and y = 1.0 samples exhibiting the lowest values of 1.4 W m−1 K−1 at 825 K. Figure of merit values are increased for the undoped solid solutions at lower temperatures when compared to the end members due to the decreased thermal conductivity, with the y = 0.5 sample reaching zT = 1.6 × 10−3 and y = 1 reaching 2.1 × 10−3 at 700 K. The largest values of the figure of merit zT for the undoped series was found for y = 2 with zT = 2.8 × 10−3 at 700 K due to the increasing n-type Seebeck coefficient. Boltztrap calculations reveal that p-doping could yield zT values above unity at 800 K in case of ZnSnAs2, comparable with ZnSnP2.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».