Laser Powder Bed Fusion Printing of CoCrFeMnNi High Entropy Alloy: Processing, Microstructure, and Mechanical Properties
Pourquoi ce travail est dans la base
Une base qui oublie comment elle a trouvé un travail ne peut pas être vérifiée. Voici les voies qui ont admis celui-ci.
Notice bibliographique
Résumé
Abstract Equiatomic CoCrFeMnNi high entropy alloy (HEA) powder was processed by laser powder bed fusion (LPBF) additive manufacturing (AM). The properties of the spherical pre-alloyed CoCrFeMnNi powder were characterized and its processability using LPBF AM was systematically investigated through the volumetric energy density (VED) based on the surface roughness, defects (micro-cracks and porosity) and densification. After optimization, LPBF processing at a VED of 104 J/mm 3 achieved highly dense and crack-free vertical and horizontal test specimens with a porosity fraction lower than 0.01% and micro-pores having a mean size of, respectively, 25.9 μm and 13.4 μm, as determined from X-ray micro-computed tomography (μCT) inspection. Scanning electron microscope (SEM) analysis of the as-built (AB) CoCrFeMnNi processed at a VED of 104 J/mm 3 showed a heterogeneous solidification microstructure, consisting of columnar grains with a cellular subgrain structure, and electron backscattered diffraction (EBSD) revealed a crystallographic texture mainly along the < 100 > direction. Post treatment with hot isostatic pressing (HIP) was effective in closing the remnant micro-pores in the bulk volume of the AB CoCrFeMnNi. Also, the cellular sub-grain structure in the AB CoCrFeMnNi completely disappeared after HIP and the resulting microstructure consisted of recrystallized equiaxed grains with annealing twins. The room temperature tensile response was anisotropic for AB CoCrFeMnNi with horizontally built specimens exhibiting higher strength and fracture strains (global and local) compared to vertically built ones; HIP reduced the anisotropy in the tensile properties and led to similar tensile strength with elongation values that were ~ 50% higher than in the AB condition. The HIPed CoCrFeMnNi also displayed higher Charpy impact toughness and absorbed energy at both room and liquid nitrogen temperatures compared to the AB material. Examination of the fracture surfaces after tensile and Charpy impact testing revealed ductile features with characteristic dimpled appearance and pointed to the important role of the remnant micro-pores on failure in the AB CoCrFeMnNi. Tribological assessments pointed to the superior low-stress abrasion resistance of AB and HIPed CoCrFeMnNi compared to 316L stainless steel (SS), which was included in this study to reinforce the analysis. SEM observations revealed that scratching and micro-fracture are the dominant wear mechanisms for the CoCrFeMnNi HEA, whereas ploughing and cutting parallel to the abrasive flow direction are the dominant mechanisms for 316L SS. To the authors’ knowledge, this study is the first to evaluate and report the low-stress abrasion resistance of any high entropy alloy. To understand the corrosion behavior, polarization curves of AB and HIPed CoCrFeMnNi were measured in 3.5 wt% NaCl and 1N H 2 SO 4 solutions, and the results were compared to those of 316L SS. The findings indicate that AB and HIPed CoCrFeMnNi outperform 316L SS in a chloride-containing environment, but not in an acid-containing environment. Additionally, observations of hydrogen permeability revealed that AB CoCrFeMnNi permeates a lower volume of hydrogen atoms (by ~ 5 times) compared to 316L SS, despite its higher (by nearly 3 times) diffusion coefficient. Electrochemical hydrogen permeation data showed that the concentration of atomic hydrogen in the sub-surface of AB and HIPed CoCrFeMnNi was, respectively, about 32 and 26 times lower than in 316L SS. This study provides important material–structure–property data and indicates a promising outlook for LPBF of the CoCrFeMnNi HEA with high-performance.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,001 | 0,001 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découle