Evaluating the Effect of Hydrogen on the Tensile Properties of Cold-Finished Mild Steel
Notice bibliographique
Résumé
One of the major sources of catastrophic failures and deterioration of the mechanical properties of metals, such as ductility, toughness, and strength, in various engineering components during application is hydrogen embrittlement (HE). It occurs as a result of the adsorption, diffusion, and interaction of hydrogen with various metal defects like dislocations, voids, grain boundaries, and oxide/matrix interfaces due to its small atomic size. Over the years, extensive effort has been dedicated to understanding hydrogen embrittlement sources, effects, and mechanisms. This study aimed at assessing the tensile properties, toughness, ductility, and susceptibility to hydrogen embrittlement of cold-finished mild steel. Steel coupons were subjected to electrochemical hydrogen charging in a carefully chosen alkaline solution over a particular time and at various charging current densities. Tensile property tests were conducted immediately after the charging process, and the results were compared with those of uncharged steel. The findings revealed a clear drop in toughness and ductility with increasing hydrogen content. Fracture surfaces were examined to determine the failure mechanisms. This evaluation has enabled the prediction of steel’s ability to withstand environments with elevated hydrogen concentrations during practical applications.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,004 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».