DETERMINATION OF FACTORS AFFECTING THE STABILITY OF WELDED TIPS OF OXYGEN LANCE
Notice bibliographique
Résumé
It has been established that the most likely cause of crack formation is differences in the chemical composition of the welding wire, the material of the Laval nozzle and the outer cage of the lance tip. For example, the difference in copper content is 6.79%. The microstructures of the weld, Laval nozzle metal, and outer lance tip rim were analyzed and compared along the cross section of the weld location. Microcracks located along the grain boundaries were detected, which is probably due to the appearance of weak compounds with low ductility and non-propagation at the grain boundaries. In the structure of welds, accumulations of oxygen inclusions along the boundaries of crystallites were found, which leads to copper embrittlement and can contribute to weld failure. Freezing a layer of converter slag with low thermal conductivity on the tip surface reduces the thermal conductivity of the formed slag metal layer and heat transfer to the cooling water. Even if there is a 1 mm layer of slag on the surface of the weld, thermal conductivity decreases by 79-95%, depending on the thickness of the slag and its properties, respectively. If there is a layer of slag on the surface of the weld, the heat transfer decreases by 51-56% (at 1 mm of slag) and by 72-88% at 20 mm, respectively.In order to prevent the formation of cracks between the Laval nozzle and the outer cage of thehandpiece, it is advisable to follow the following recommendations when performing welding operations. In the simplest case, the first welded layer should be performed using a non-consumable electrode (tungsten or graphite) in an argon or helium atmosphere, which will ensure the formation of a reliable, tight weld around the entire circumference of the nozzle. To reduce stresses in the weld, subsequent welded layers should be performed in alternating directions. A more effective option is the technology according to which, after the first weld is applied, the nozzle is connected to the tip from the inside with a partial (discrete) or continuous weld, which minimizes the likelihood of failures and can ensure the sealing of the tip when the initial cross-section of the Laval nozzles increases to the critical ignition diameter. The implementation of an internal weld will reduce mechanical loads on the external weld, especially when using metal hose expansion joints, and increase the strength of the welded joint as a whole.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,001 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,001 |
| Études des sciences et des technologies | 0,000 | 0,001 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».