Microstructures Resulting from the Use of Solder Balls of One Composition with Paste of a Different Composition on a Copper Substrate
Notice bibliographique
Résumé
ABSTRACT With the development and use of a variety of Pb-free solders, it is probable that some solder joints in electronic assemblies may be made with solders of two different compositions, one of which may be eutectic Pb-Sn. To investigate some possible resulting microstructures, small balls of four different SAC Pb-free solders were each melted with eutectic Pb-Sn solder paste, as well as with various SAC pastes, on a copper substrate. Two paste levels were used, 20 and 29 weight percent of the total sample weight. In all cases, the sample was held for 90 seconds at a temperature above the melting point of the solder paste. For samples made with PbSn paste, two different values of maximum temperature were used, 210°C and 220°C, while for samples made with SAC paste, the maximum temperatures used were 235°C and 245°C. The resulting microstructures were evaluated metallographically using both optical and scanning electron microscopes. It was observed that the use of Pb-Sn solder paste introduced some Pb-Sn eutectic microstructure and changed the ternary eutectic present from Ag 3 Sn-Cu 6 Sn 5 -Sn, normally observed in SAC alloys, to Ag 3 Sn-Pb-Sn. The high Sn content of the SAC alloys used led to rapid dissolution of the copper substrate, often resulting, on cooling, in formation of primary Cu 6 Sn 5 crystals and Cu 6 Sn 5 -Sn binary eutectic regions. Similar experiments were also carried out using balls of the Sn-Zn-Al solder alloy.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,001 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,001 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».