Microstructural Analysis of Linear Friction Welded Joint in Nickel-Base Inconel 738 Superalloy
Notice bibliographique
Résumé
Inconel 738 (IN 738), like other precipitation-hardened nickel-base superalloys that contain a substantial amount of Al and Ti, is very difficult to weld due to its high susceptibility to heat-affected zone (HAZ) cracking during conventional fusion welding processes. The cause of this cracking, which is usually intergranular in nature, has been attributed to the liquation of various phases in the alloy, subsequent wetting of the grain boundaries by the liquid and decohesion along one of the solid-liquid interfaces due to on-cooling tensile stresses. To address the problem of liquation cracking in weldments, recent developments in welding research have resulted in supposedly exclusive solid-state friction joining processes, such as linear friction welding (LFW), for joining crack susceptible structural alloys. The objective of this work was therefore to investigate the weldability of the difficult-to-weld IN 738 superalloy by LFW and to analyze the resulting microstructural changes in the alloy due to the welding process. LFW was performed on Linear Friction Welding Process Development System (PDS) at the Aerospace Manufacturing Technology Centre of the Institute for Aerospace Research, National Research Council (NRC) of Canada. In order to study and decouple the effect of non-equilibrium thermal cycle and imposed compressive stress during the joining, physical simulation of the LFW process was performed by using Gleeble 1500-D Thermo-Mechanical Simulation System at the University of Manitoba. Detailed microstructural study of welded and Gleeble-simulated materials was carried out. Correlation between the simulated microstructure and that of the weldments was obtained, in that, a significant grain boundary liquation was observed in both the simulated specimens and actual weldments due to non-equilibrium reaction of second phase particles, including the strengthening gamma prime phase. These results show that in contrast to the general assumption of LFW being an exclusively solid-state joining process, intergranular liquation, caused by non-equilibrium phase reaction(s), occurred during the process. However, despite a significant occurrence of liquation in the alloy, no HAZ cracking was observed. Nevertheless, the result showed that crack-free welding by linear friction welding is not due to preclusion of grain boundary liquation as has been commonly assumed and reported. Instead, resistance to cracking can be related to the counter-crack-formation effect of the imposed strain and to a concept observed and reported for the first time in this work, which is strain-induced rapid solidification. Furthermore, microstructural evolution during joining cannot be understood without considering the concept of non-equilibrium liquation reaction and strain-induced rapid solidification of the metastable liquid, which are carefully elucidated in this thesis.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,001 | 0,001 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».