The Effects of Aging on the Microstructure and Mechanical Properties of Bi-Containing Sn-Rich Alloys
Notice bibliographique
Résumé
ABSTRACT A significant reliability concern with lead-free solder alloys such as SAC 305 is the degradation of mechanical properties after aging at both elevated and room temperature, due to the coarsening and recrystallization of the microstructure. It has been shown in earlier studies that the inclusion of bismuth (Bi) in these alloys leads to a stabilization of the microstructure and subsequent maintenance of as-cast properties after aging. The goal of this paper and ongoing research is twofold – to ascertain whether these trends hold at a large range of aging temperatures and times, and to understand the underlying metallurgical mechanisms that lead to these effects. This paper examines the effects of aging on the microstructure and hardness of Bi-containing Sn-rich alloys. The alloys studied were Sn-1Bi, Sn-5Bi, Sn-0.7Cu-1Bi, and Sn-0.7Cu-5Bi, as well as a baseline alloy, SAC 305. These alloys were aged both at room temperature (between 10 and 365 days) and at elevated temperature (100°C and 125°C, between 1 and 14 days). As-cast microstructure and properties were also included. Cooling after elevated temperature aging was performed in air. The microstructure was evaluated using Scanning Electron Microscopy, and hardness was measured using a Rockwell hardness tester HR15X with a ¼” carbide ball indenter. For Bi-containing alloys, bismuth precipitates became more uniformly distributed as aging proceeded, and hardness did not undergo any appreciable changes. SAC 305, on the other hand, showed a predictable decay in hardness after all aging treatments.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».