Kinetics of crack propagation in hydraulic turbine runner material exposed to river water
Notice bibliographique
Résumé
Hydraulic turbines are critical for Quebec's electricity production, as hydroelectricity accounts for 95% of its power generation. During operation, Francis turbines are subjected to cyclic loading and exposed to river water, leading to crack initiation and propagation. The integrity of these components is assessed through regular inspections, which provide updates on life predictions derived from damage tolerance models based on fatigue crack growth rate (da/dN) as a function of the applied stress intensity factor range (?K). This study investigates for the first time the influence of river water and material’s microstructure on corrosion-fatigue crack growth (CFCG) behavior of 13Cr-4Ni low-carbon martensitic stainless steel. This research helps improve damage tolerance models by accounting for environmental effects. Fatigue crack growth tests were conducted in air and river water at two ?K values of 8 MPa·m0.5 and 15 MPa·m0.5 on steels with minimal (SM) and maximal (SRA) reformed austenite (RA) fractions of 3% and 20%, respectively. To investigate the environment’s influence, a setup was developed where the sample was partially immersed using an enclosure and the synthesized river water was circulated using a pump. The load frequency was varied from 10 Hz to 0.1 Hz and two load ratios (R) of 0.1 and 0.7 were applied. Measurements showed that CFCG rate (CFCGR) was mitigated by crack closure at frequencies of 10 Hz and 1 Hz, resulting in fatigue crack growth rates (FCGR) comparable to those in air. After accounting for crack closure, environmental effects on crack propagation kinetics were revealed. On average, fatigue cracks propagated faster in water for both microstructures. The scatter of data compromises the robustness of this conclusion for SM. In SRA material, significant environmental effect was observed below effective ?K (?Keff) of 9 MPa·m0.5, attributed to longer crack tip exposure times due to slower crack propagation speed (da/dt). A comparison of CFCGRs between SM and SRA revealed that above ?Keff of 6.5 MPa·m0.5, SRA exhibited slower CFCGR due to greater crack closure, extensive crack branching, and RA-to-martensite transformation. Given the negligible environmental impact at high load frequencies, Hydro-Québec can safely use FCGR data from air tests. This experimental work correlating microstructure and crack propagation reveals that higher RA fractions led to slower CFCGR and FCGR. Developing RA-enriched alloys and optimizing hydraulic turbine manufacturing by new developed alloys could improve turbine runner durability. To complement this work, tests under variable R conditions better representing actual turbine loading should be performed.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,001 | 0,001 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,001 | 0,001 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,001 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,007 | 0,009 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; les deux têtes enseignantes s’accordent sur ce qui est montré ici.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».