Investigation of Stress Assisted Grain Boundary Oxidization (SAGBO) Cracking in Mar-M002 High Pressure Turbine Blades
Bibliographic record
Abstract
Modern superalloys have enabled High Pressure Turbine (HPT) blades in Gas Turbine Engines (GTE) to operate at higher temperatures. Unfortunately the complexity of these materials can make it difficult to understand the failure mechanisms of these blades. HPT blades made of the nickel based superalloy Mar-M002 have been found to suffer from Stress Assisted Grain Boundary Oxidation (SAGBO) cracking. HPT blades removed from an RB211-24C aero-derivative industrial GTE were sectioned and the cracks and microstructure were studied using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS). No cracks were found on the external surface of the blade which had been coated with an oxidation resistant material. Surface irregularities were found along the walls of the inner cooling channels throughout the entire blade. Larger SAGBO cracks were observed to be near the lower 25% span of the blade and had initiated from the surfaces of the cooling channels. SEM/EDS analysis showed that these cracks had large amounts of alumina and Hafnium-rich particles within them. It is evident that these cracks occurred in locations where the combination of high stress and high temperature led to higher rates of oxygen diffusion and subsequent oxidation of grain boundary carbides. Hafnium Carbide precipitates along the grain boundaries expanded as they converted into Hafnium Oxide, thus further increasing the stress. It is envisaged that this increase in stress along the grain boundary has caused the cracks to initiate and coalesce. Based on this observation, it is believed that the inner cooling channels of these HPT blades could benefit from the application of an oxidation resistant coating in order to prevent or delay the formation of these cracks.
Fetched live from OpenAlex and de-inverted. Abstracts are not stored in this database: the inverted indexes are 8.6 GB of the frame’s 9.3 GB of text, and the host has 13 GB free.
How this classification was reachedexpand
Full frame distilled prediction
Teacher imitationNot calibrated prevalence, not ground truth. Human validation pending. Learned from the 10,348 direct Codex labels and 10,348 direct Gemma labels. Candidate is the union of thresholded teacher heads; consensus is their intersection. These outputs are machine_predicted_unvalidated and are not human labels or direct frontier model labels.
Codex and Gemma teacher scores by category
| Category | Codex | Gemma |
|---|---|---|
| Metaresearch | 0.000 | 0.000 |
| Meta-epidemiology (narrow) | 0.001 | 0.001 |
| Meta-epidemiology (broad) | 0.001 | 0.000 |
| Bibliometrics | 0.001 | 0.000 |
| Science and technology studies | 0.000 | 0.000 |
| Scholarly communication | 0.000 | 0.001 |
| Open science | 0.000 | 0.000 |
| Research integrity | 0.000 | 0.000 |
| Insufficient payload (model declined to judge) | 0.000 | 0.000 |
Machine scores (provisional)
The two teacher heads of the student model, read on this work. A score orders the frame for review; it never asserts a category, and the validation status ships verbatim with every row.
Baseline scores from an immature model (maturity gate not passed, 7 training rounds). Scores rank; they never assert a category.
score_only:v0-immature-baseline · verbatim from the scoring run: score_only means the number may rank works, and no category label ships from itClassification
machine, unvalidatedMachine predicted; a candidate call from one teacher head, not a consensus.
How this classification was reached, model by model and score by score, is at the end of the page under "How this classification was reached".