Deflected Stress Corrosion Cracks in the Pipeline Steel
Notice bibliographique
Résumé
This research reports a special case of stress corrosion cracks (SCC) in the pipeline steels that had propagated in the direction deviated from the pipe radial direction. It was characterized that the cracks were intergranular in nature with relatively wide crack crevice. Most of crack being characterized consisted of two segments: a crack segment near pipe surface that is normal to the axis of hoop stress, and the subsequent segment that is inclined to the axis of the hoop stress. The segment near the surface was usually less than 1.5 mm long, and the inclined one was up to 10 mm in length. The angle of the inclined segment was dominantly in the range of 30° to 60°. To understand the mechanisms related to the deflected crack growth, the microstructure of the pipeline steels was studied. It was found that The pipeline steel is characterized with a sandwich-like microstructure, for which it is harder at the surface (∼ 1.5 mm thick) and progressively softer towards the center of the wall. This particular structure might have caused a complex loading condition to the pipe wall material such that yielding of the soft material become possible, particularly when crack has propagated into the soft region of the pipe wall. As a result, corrosion attack may take place in a direction consistent with the maximum shear stress, and cracking preceded by the concurrent interaction between corrosion attack and mechanical damage.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,001 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,001 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,001 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».