Abstract Much has been studied on the individual effects of creep and fatigue on alloy life. However, not much is known of the combined effects of these two mechanisms. Therefore, a study was put into place to determine the effects of dwell on fatigue life and deformation mechanisms, for IN617, a solid-solution strengthened Ni-base alloy used widely in the power generation and aerospace industries. Low cycle fatigue (LCF) tests were conducted from 649–982°C with either tensile or compressive dwell. Fracture surfaces of the test specimens as well as longitudinal and transverse sections were examined via scanning electron microscopy to determine the damage and failure mechanisms. Test results confirmed tensile dwell lives that were significantly lower than those seen in compressive dwell. The mechanics for the reduction in cyclic life for tensile dwell was attributed to creep damage accumulation at grain boundaries that led to widespread intergranular cracking and failure. Tensile dwell life reductions were largest in tests at moderate (649–760°C) temperatures. The failed specimens for this temperature range showed the most evidence of grain boundary cavitation and intergranular cracking. At higher test temperatures, the tensile dwell sensitivity for IN617 was significantly reduced or almost entirely eliminated at high temperatures (871–982°C). This was attributed to the lower stresses that developed at these temperatures for a given strain range. The LCF testing and subsequent analysis indicated that a substantial tensile stress during dwell time coupled with moderate temperatures, to allow for diffusion creep, lead to grain boundary damage that can reduce cyclic life.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,001 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».