Room temperature transport measurements on Bridgman-grown CuInSe 2 with added sodium
Notice bibliographique
Résumé
Thermoelectric power, Hall coefficient and resistivity measurements were carried out on material cut from monocrystalline ingots of CuInSe2. The ingots were grown using a vertical-Bridgman procedure, whereby Cu, In and Se were melted and directionally cooled within a sealed quartz ampoule. When stoichiometric proportions of the starting elements were used, the material was always p-type, with hole concentrations of the order of 1017-1018 cm-3. However, the incorporation of a sufficient amount of sodium (0.3 at. %) into the melt was seen to result in n-type material, with electron concentrations of the order of 1016. This conversion from p to n was hindered by the inclusion Se above stoichiometry into the ampoule, and more Na was required for the material to change type. The mobility of the p-type samples, with low sodium additions (0-0.2 at. %), was on average 17 cm2V-1s-1, and was seen to be higher for material grown from melts containing excess Se, corresponding to the chemical formula CuInSe2.2, than from stoichiometry. SEM/EDX (Scanning electron microscope / Energy-dispersive X-ray spectroscopy) analysis of the ingots after growth indicated no sodium residing within the interior of the bulk material, but a significant amount was found on the exterior surface in the case of an ingot grown with CuInSe2.05 and 5 at. % Na. Various deposits found within the ampoules after growth were analyzed, including a copper-rich precipitate found only in ampoules which included a high concentration of Na and a low concentration of excess Se, resulting in n-type material.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,001 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,001 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,001 |
| Science ouverte | 0,001 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,002 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».