Vanadium oxide films for optical modulation applications
Notice bibliographique
Résumé
Thin films of vanadium oxide were prepared and studied for the electro-optical properties of semiconductor-metal transition. Vanadium oxide films with thickness of ~ 0.15μm were deposited on SiO2/Si substrates by reactive RF magnetron sputtering using a pure vanadium target under various ratios of argon and oxygen gases. The oxygen content in the mixed atmosphere has a significant influence on the semiconductor-metal transition characteristics. Both thermochromic and electrochromic modes were studied. In thermochromic mode, the oxide film deposited in an O2/Ar ratio of 1.2% exhibits 90% optical transmission in semiconducting state at room temperatures, while very low transmission at 5% in metallic state at 65°C, in the wavelength region of 8 to 12μm. In the near infrared region of 1 to 2μm, the transmission is about 60% in the semiconducting state and a few percents in the metal state. A corresponding three-order variation of resistivity was observed over the transition. The refractive indices (n and k) of the vanadium oxide films were measured using an ellipsometer in the near infrared region between 1 and 2 μm in both states. The index n decreases in metal state while k increases. The electrochromic phase transition of vanadium oxide was investigated by applying a pulsed voltage to minimize the heating effect. The required charge density for the phase transition is consistence with the Mott metal-insulator model. Longwave IR switching and modulation were demonstrated by electrically induced semiconductor-metal transition.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,002 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».