Production of a new 3D electrode skeleton of Ni with very high electrochemical surface area for oxygen evolution
Notice bibliographique
Résumé
Long and stable fibers (Tapes) of nickel with a thickness that can reach less than one hundred nanometers were produced through directional solidification of Ni-Al hypereutectic alloy on the surface of Ni and then, leaching the alloy in potassium hydroxide solution. Experimental results illustrated that the structure of the tapes is Raney nickel. In other words, a 3D structure consisting of a large number of Nano-dimensional tapes with a Nano-porous and Nano-crystalline structure was created. The activity of this structure was evaluated for oxygen evolution in alkaline media. The results showed that by increasing the number of Tapes per 〖cm〗^2 (density of Tapes), electrochemical surface area and double layer capacitance increase. As the density of Tapes increases, the OER overpotential decreases, but with further increase in density of Tapes, the OER overpotential increases again. Re-increase in overpotential was associated to trapping of oxygen bubbles. The best sample showed an overpotential 240 mV at 10 mA/〖cm〗^2 and 350 mV at 500 mA/〖cm〗^2. Also, this sample worked without any sign of degradation at 500 mA/〖cm〗^2 for 6 days (144 hours).
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,000 | 0,000 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,000 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».