Effect of Accelerated Cooling on Linepipe Steel Mill Scale and Resulting Localized Corrosion Susceptibility
Notice bibliographique
Résumé
The structure and composition of mill scale on linepipe steel formed with and without accelerated cooling conditions (ACC) was investigated and correlated to localized corrosion susceptibility. The mill scale structure/composition was investigated using scanning electron microscopy equipped with x-ray energy dispersive spectroscopy and electron backscatter diffraction, as well as x-ray diffraction. Localized dissolution of the mill scale was investigated using electrochemical techniques including open-circuit potential measurements, electrochemical impedance spectroscopy, and electrochemical noise measurements in a corrosive phase solution. The various surface analytical and electrochemical techniques indicated that the mill scale formed without ACC consists of a relatively crack-free, thick inner wüstite layer with a thinner magnetite outer layer. However, the mill scale formed with ACC comprised a magnetite layer containing islands of retained wüstite, with some evidence of magnetite/iron eutectoid formation and which exhibited a relatively high density of through-scale cracks. These cracks can provide direct paths that connect the corrosive solution to the steel substrate, leading to a more rapid breakdown of the mill scale. Additionally, the cracks can form a crevice between the mill scale and the steel surface, providing sites for pit initiation and growth. Coefficient of thermal expansion mismatch thermal stress calculations indicate that a magnetite-based scale is more susceptible to cracking/spalling than a wüstite-based scale, resulting in the ACC plate being more susceptible to localized corrosion.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction distillée sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Apprise à partir de 10 348 étiquettes directes de Codex et de 10 348 étiquettes directes de Gemma. Le mode candidate est l'union des têtes enseignantes seuillées; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont ni des étiquettes humaines ni des étiquettes directes de modèles de pointe.
Scores Codex et Gemma par catégorie
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,002 | 0,001 |
| Méta-épidémiologie (sens strict) | 0,000 | 0,000 |
| Méta-épidémiologie (sens large) | 0,001 | 0,000 |
| Bibliométrie | 0,000 | 0,000 |
| Études des sciences et des technologies | 0,000 | 0,000 |
| Communication savante | 0,000 | 0,000 |
| Science ouverte | 0,000 | 0,000 |
| Intégrité de la recherche | 0,000 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,000 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule tête enseignante, pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».