Recent Experience from Field Application and Laboratory Testing on the Corrosion Risk of Stainless Steel UNS S82551 in Water Alternating Gas Service
Notice bibliographique
Résumé
Abstract Duplex stainless steel UNS1 S82551 tubing has been used since 2017 in Water Alternating Gas (WAG) injection wells on the Norwegian continental shelf. After approximately five years of operation, leaks were reported in two wells. Investigations were performed to determine the root cause of these failures, including a review of the metallurgy and fluids used during well construction and operation phases. The metallurgy included, amongst others, the following alloys: UNS S82551, UNS S39274 and UNS N09925. Inspection of the retrieved well components revealed that the leaks were caused by crevice corrosion to the tubing threaded connections. UNS S82551 is expected to be corrosion resistant in WAG service utilizing treated seawater and dried gas. However, earlier extensive laboratory testing showed that this alloy can be sensitive to crevice corrosion under seawater treatment deviations. Subsequent laboratory corrosion testing including all fluids in contact with the well materials during construction showed no impact on crevice corrosion. The root cause analysis revealed that the operating treatment procedure allowed residual chlorine in the injected seawater. Immersion and electrochemical testing confirmed that the conditions of exposure induced by the operation procedure led to crevice corrosion of alloy UNS S82551, and this was the root cause of the tubing leaks.
Récupéré en direct depuis OpenAlex et désinversé. Les résumés ne sont pas conservés dans cette base de données : les index inversés représentent 8,6 Go des 9,3 Go de texte de la base, et le serveur dispose de 13 Go libres.
Comment cette classification a été obtenuedéplier
Prédiction machine sur la base complète
Imitation des enseignantsNi prévalence calibrée, ni vérité terrain. Validation humaine à venir. Le volet Gemma est une étiquette directe du modèle pour chaque travail de la base, lue sur la notice réduite au titre. Le volet Codex est un classifieur appris des 10 348 étiquettes directes de Codex et calibré sur les taux pondérés de l'échantillon; les champs sans appui suffisant ne portent aucun appel Codex. Le mode candidate est l'union des deux volets; le consensus est leur intersection. Ces sorties portent le statut machine_predicted_unvalidated et ne sont pas des étiquettes humaines.
Scores du classifieur distillé par catégorie (deux têtes)
| Catégorie | Codex | Gemma |
|---|---|---|
| Métarecherche | 0,004 | 0,003 |
| Méta-épidémiologie (sens strict) | 0,001 | 0,000 |
| Méta-épidémiologie (sens large) | 0,000 | 0,000 |
| Bibliométrie | 0,001 | 0,001 |
| Études des sciences et des technologies | 0,001 | 0,001 |
| Communication savante | 0,001 | 0,001 |
| Science ouverte | 0,001 | 0,001 |
| Intégrité de la recherche | 0,001 | 0,000 |
| Charge utile insuffisante (le modèle a refusé de juger) | 0,001 | 0,001 |
Scores machine (provisoires)
Les deux têtes enseignantes du modèle étudiant, lues sur ce travail. Un score ordonne la base pour la relecture; il n'affirme jamais une catégorie, et le statut de validation accompagne chaque rangée tel quel.
Scores de référence d'un modèle non mature (critères de maturité non atteints, 7 itérations). Un score ordonne; il n'affirme jamais une catégorie.
score_only:v0-immature-baseline · tel quel depuis la passe de notation : score_only signifie que le nombre peut ordonner les travaux, et qu'aucune étiquette de catégorie n'en découleClassification
machine, non validéePrédiction automatique; un appel candidat d’une seule source (Gemma direct ou Codex distillé), pas un consensus.
Le détail, modèle par modèle et score par score, se trouve en fin de page sous « Comment cette classification a été obtenue ».