Effect of Alumina Particle Size on the Bond Strength between Autopolymerized Acrylic Resin and Commercially Pure Titanium
Why this work is in the frame
A frame that forgets how it found something cannot be audited. These are the routes that admitted this work.
Bibliographic record
Abstract
PURPOSE: To address the following null hypothesis: when the Rocatec bonding system is used, the various sizes of aluminum oxide particles used to roughen the surface area of the commercially pure (CP) titanium prior to bonding to autopolymerized resin have no effect on the average shear bond strength. MATERIALS AND METHODS: One hundred specimens were randomly allocated to five equally sized groups: Ti-no air abrasion (group A), Ti-air-abraded with 50 μm (group B), Ti-110 μm (group C), Ti-250 μm (group D), and Co-Cr-50 μm (group E) grain-size aluminum oxide. Rocatec Plus tribochemical coating was applied to all of the specimens, followed by a RelyX primer and Sinfonyopaquer. Autopolymerized denture base resin was then bonded to the treated titanium surfaces. All specimens underwent thermocycling (10,000 cycles), shear bond testing, and mode of failure examination under stereoscopic microscopy. RESULTS: The average bond strength of group D (250 μm) was significantly different compared to all other groups, except group C (p = 0.057, trending significance). The average bond strength of group D was substantially higher than that in the other groups (p < 0.01). The weakest bond was observed when the specimens did not receive any air abrasion (group A). Maximum load (N) showed the same significant results as the shear bond strength at maximum load (MPa). The average extension at maximum load (mm) and the time at maximum load(s) for group A were significantly different than that of all other groups. Group A had lower average values than any other group (p = 0.003). More cohesive and mixed, rather than adhesive, modes of failure were observed as the size of the aluminum oxide particles increased. CONCLUSION: When the Rocatec system is used, using a combination of chemical and micromechanical adhesion is essential for the success of the bond between the autopolymerized acrylic resin and CP Ti. The micromechanical interlock can be improved significantly when the Ti surface is air abraded with larger particles (250 μm) than the currently used alumina particle size.
Fetched live from OpenAlex and de-inverted. Abstracts are not stored in this database: the inverted indexes are 8.6 GB of the frame’s 9.3 GB of text, and the host has 13 GB free.
Full frame distilled prediction
Teacher imitationNot calibrated prevalence, not ground truth. Human validation pending. Learned from the 10,348 direct Codex labels and 10,348 direct Gemma labels. Candidate is the union of thresholded teacher heads; consensus is their intersection. These outputs are machine_predicted_unvalidated and are not human labels or direct frontier model labels.
Codex and Gemma teacher scores by category
| Category | Codex | Gemma |
|---|---|---|
| Metaresearch | 0.001 | 0.001 |
| Meta-epidemiology (narrow) | 0.000 | 0.000 |
| Meta-epidemiology (broad) | 0.000 | 0.000 |
| Bibliometrics | 0.000 | 0.000 |
| Science and technology studies | 0.000 | 0.000 |
| Scholarly communication | 0.000 | 0.000 |
| Open science | 0.000 | 0.000 |
| Research integrity | 0.000 | 0.000 |
| Insufficient payload (model declined to judge) | 0.000 | 0.000 |
Machine scores (provisional)
The two teacher heads of the student model, read on this work. A score orders the frame for review; it never asserts a category, and the validation status ships verbatim with every row.
Baseline scores from an immature model (maturity gate not passed, 7 training rounds). Scores rank; they never assert a category.
score_only:v0-immature-baseline · verbatim from the scoring run: score_only means the number may rank works, and no category label ships from it